Translations between different materials standards

JUMU

2019/07/04 22:56:59

Translations betweendifferent materials standards.

SS 14: Swedishstandard is to be replaced by EN.
EN: European standards.
GB: The people's republic of Chinastandards.
DIN: DeutschIndustrie Norm Germany.
W.Nr: Werkstoffnummer Germany.
AISI/SAE: USA.

ral structural stee
SS 14	EN	GB	DIN	W.Nr	AISI/SAE
1312	S235JRG2	Q 235 A Q 235 B	RSt 37-2	1.0038 (1.0116)	A570 Gr.36
1370		Q215A	RSt34-2	1.0028	A283M
1412	S275	Q255A	St 44-2	1.0044	1020
1430		Q275A	S275J2G3	1.0144	K02901
1265		10	C10	1.0301	1010
1350		15	C15	1.0401	1011
1435		20	C22E	1.1151	1020
1572		35	C35E	1.1181	1035
1660		45	C45E	1.1191	1045
1665		55	C55E	1.1203	1055
1674	C50E	50	C50E	1.1210	1050
1770		65	CK67	1.1231	1065
1778		70			1070
2120		35Mn2	36Mn5	1.1167	1335
2132		20Mn	20Mn5	1.1133	1022
2134	S355N	16 Mn	StE 355	1.0545
2172	S355JR	Q 275	S355JR	1.0045	1518

at treatment s
SS 14	EN	GB	DIN	W.Nr	AISI/SAE
2216		12CrMo	13CrMo44	1.7335	4119
2225	25CrMo4	25CrMo	25CrMo4	1.7218	4130
2230		50CrVA	51CrV4	1.8159
2234		35CrMoV	34CrMo	1.7220	4135
2242	X40CrMoV5-1	4Cr5MoSiV1		1.2344	H 13
2244		42CrMo	42CrMo4	1.7225	4140
2245		40Cr	41Cr4	1.7035	5140
2506		20CrNiMo	21NiCrMo2	1.6523	8620
2511		15CrMn	16MnCr5	1.7131
2541	34CrNiMo6	35CrMo	34CrNiMo6	1.6582	4340
2940		38CrMoAl	41CrAlMo7	1.8509

aring steel
SS 14	EN	GB	DIN	W.Nr	AISI/SAE
SKF3		GCr15	W3	1.3505	E52100

ool stee
SS 14	EN	GB	DIN	W.Nr	AISI/SAE
1778		T8	C80W2	1.1625
1880		T10	C105E2	1.1645
1885		T12	C110W1	1.1550
2062		9SiCr	90Cr3	1.2056
2260		Cr5Mo1V	X100CrMoV5-1	1.23633	A2
2140		9CrWMn	100MnCrV4	1.2510
2310		Cr12MoV	StE 355	1.2601	D3

tainless stee
SS 14	EN	GB	DIN	W.Nr	AISI/SAE
2302		1Cr13	X10Cr13	1.4006	410
2320		1Cr17	X6Cr17	1.4016	430
2333	X5CrNi18-10	0Cr18Ni9	X 5 CrNi 18 10	1.4301	304
2337	X12CrNiTi	1Cr18Ni9Ti	X12CrNiTi	1.4878	321

gh Speed St
SS 14	EN	GB	DIN	W.Nr	AISI/SAE
2722		W6Mo5Cr4V2	S6-5-2	1.3343	M2
2750		W18Cr4V	S18-01	1.3355	T1

Observe that no quality should be castings.

hemical composition
GB	C %	Si %	Mn %	P %	S %	Cr %	Mo %	Ni %	Cu %	N %	Others %
Q215A	0.09-0.15	≤0,30	0.25-0.55	≤0.045	≤0.05
Q 235A	0.14-0.22	≤0.30	0.30-0.65	≤0.045	≤0.05
Q 235B	0.12-0,20	≤0,30	0,30-0,70	≤0,045	≤0,045	-	-	-	-		-
Q 255A	0.18-0.28	≤0,30	0.40-0.70	≤0,045	≤0,05
10	0.07-0.14	0.17-0.37	0.35-0.65	≤0.035	≤0.035	≤0.15		≤0.25	≤0.25
15	0.12-0.19	0.17-0.37	0.35-0.65	≤0.035	≤0.035	≤0.15		≤0.25	≤0.25
20	0.17-0.24	0.17-0.37	0.35-0.65	≤0.035	≤0.035	≤0.15		≤0.25	≤0.25
35	0.32-0.40	0.17-0.37	0.50-0.80	≤0.035	≤0.035	≤0.15		≤0.25	≤0.25
45	0,42-0,50	0,17-0,37	0.50-0,80	≤0.035	≤0.035	≤0.25-	-	≤0.30	≤0.25	-	-
50	0.47-0.55	0.17-0.37	0.50-0.80	≤0.035	≤0.035	≤0.25		≤0.25	≤0.25
55	0.52-0.60	0.17-0.37	0.50-0,80	≤0.035	≤0.035	≤0.25		≤0.25	≤0.25
60	0.57-0.65	0.17-0.37	0.50-0.80	≤0.035	≤0.035	≤0.25		≤0.25	≤0.25
70	0.67-0.75	0.17-0.37	0.50-0,80	≤0.035	≤0.035	≤0.25		≤0.25	≤0.25
45H	0.42-0.50	0,17-0,37	0.50-0.85
20Mn	0.17-0.24	0,17-0,37	0.70-1.00	≤0.035	≤0.035	≤0.25		≤0.25	≤0.25
16Mn	0.12-0,20	0.20-0.60	1.20-1.60	≤0,05	≤0,05	-	-	-	-
Q 275	0.28-0.38	≤0,35	0.50-0.80	≤0,045	≤0,05						-
Q 275A	≤0.24	≤0.35	≤1.50	≤0.45	≤0.45
12CrMo	0.08-0.15	0.17-0.37	0.40-0.70	≤0.04	≤0.04	0.40-0.70	0.40-0.55
25CrMo	0.22-0.29	0.17-0.37	0.50-0.80			0.90-1.20	0.15-0.30
30CrMo	0.26-0.34	0.17-0.37	0.40-0.70			0,80-1,10	0,15-0,25	-	-	-	-
35CrMo	0.32-0.40	0.17-0.37	0.40-0.70			0.80-1.10	0.15-0.25
42CrMo	0.38-0.45	0.17-0.37	0.50-0.80			0.90-1.20	0.15-0.25
35Mn2	0.32-0.39	0.17-0.37	1.40-1.80
50CrVA	0.46-0.54	0.17-0.37	0.50-0.80	0.03	0.03	0.80-1.10		0.35	0.25		V0.10-0.20
35CrMoV	0.30-0.38	0.17-0.370	0.40-0.70			1.00-1.30	0.20-0.30				V0.10-0.20
40Cr	0.37-0.44	0.17-0.37	0.50-0.80			0.80-1.10
20CrNiMo	0.17-0.23	0.17-0.37	0.60-0.95			0.40-0.70	0.20-0.30	0.35-0.75
15CrMn	0.12-0.18	0.17-0.37	1.10-1.40			0.40-0.70
38CrMoAl	0.35-0.42	0.20-0.45	0.30-0.60			1.35-1.65	0.15-0.25				Al0.70-1.10
4Cr5MoSiV1	0.32-0.45	0,80-1,20	0.20-0.50	≤0,03	0,03	4.75-5,50	1,10-1,75	-	-	-	V 0,80-1,20
Cr5Mo1V	0.95-1.05	≤0.50	≤1.0	≤0.03	≤0.03	4.75-5.50	0.90-1.40				V0.15-0.50
9CrWMn	0.85-0.95	≤0.40	0.90-1.20	≤0.03	≤0.03	0.50-0.80					W0.50-0.80
Cr12MoV	1.45-1.70	≤0.40	≤0.40	≤0.03	≤0.03	11.0-12.5	0.40-0.60				V0.15-0.30
0Cr18Ni9	≤0.07	≤1,00	≤2,00	≤0.035	≤0.03	17,0-19,0	-	8,00-11,0	-	-	-
1Cr18Ni9Ti	≤0.12	≤1.00	≤2.00	≤0.035	≤0.03	17.0-19.0		8.00-11.0
GCr15	0.95-1.05	0.15-0.35	0.25-0.45	≤0.025	≤0.025	1.40-1.65
T8	0.75-0.84	≤0.35	≤0.40	≤0.035	≤0.03
T10	0.95-1.04	≤0.35	≤0.40	≤0.035	≤0.03
T12	1.15-1.24	≤0.35	≤0.40	≤0.035	≤0.03
9SiCr	`0.85-0.95	1.20-1.60	0.30-0.60	≤0.30	≤0.30	0.95-1.25
1Cr13	≤0.15	≤1.00	≤1.00	≤0.035	≤0.03	11.5-13.5
1Cr17	≤0.12	≤0.75	≤1.00	≤0.035	≤0.03	16.0-18.0
W6Mo5Cr4V2	0.80-0.90	≤0.40	≤0.40	≤0.30	≤0.30	3.80-4.40	4.50-5.50				W5.50-6.75 V1.75-2.20
W18Cr4V	0.70-0.80	≤0.40	≤0.40	≤0.30	≤0.30	3.80-4.40	≤0.30				W17.5-19.0 V1.0-4.4

Mechanical properties

GB-steel	Condition	Delivery form	Thickness of material (mm)	σs (N/mm2) ≥	σb (N/mm2) ≥	δs % ≥	Hardness HB ≤
Q 215A	Untreated or heat-treated		≤ 16 16-4 0 40-60 60-100 100-150 >150	215 205 195 185 175 165	335-450	31 30 29 28 27 26	99.8-133
Q 235A	Untreated or heat-treated		≤ 16 16-4 0 40-60 60-100 100-150 >150	235 225 215 205 195 185	375-500	26 25 24 23 22 21	150
Q 235B	Untreated or heat-treated		≤ 16 16-4 0 40-60 60-100 100-150 >150	235 225 215 205 195 185	375-500	26 25 24 23 22 21	150
Q 255A	Untreated or heat-treated		≤ 16 16-4 0 40-60 60-100 100-150 >150	255 245 235 225 215 205	410-550	24 23 22 21 20 19	163
Q 275	Untreated or heat-treated		≤ 16 16-4 0 40-60 60-100 100-150 >150	275 265 255 245 235 225	490-630	20 19 18 17 16 15	186
Q 275A	Untreated or heat-treated			275	410-540	22	160
10	Untreated or heat-treated	Bar	25	205	335	31	137
15	Untreated or heat-treated	Bar	25	225	375	27	143
20	Untreated or heat-treated	Bar	25	245	410	25	156
35	Untreated or heat-treated	Bar	25	315	530	20	197
45	Untreated or heat-treated	Bar	25	355	600	16	229
50	Untreated or heat-treated	Bar	25	375	630	14	241
55	Untreated or heat-treated	Bar	25	380	645	13	255
60	Untreated or heat-treated	Bar	25	400	675	12	255
70	Untreated or heat-treated	Bar	25	420	715	9	269
20Mn	Untreated or heat-treated		25	275	450	24	197
16Mn	Untreated or heat-treated	Tube		343	509.6	21
12CrMo	Untreated or heat-treated Normalizing +tempering		≤100 100-300	245 275 275	411.6 440 440	21 20 20	159 159
25CrMo	Thermal refining		17-40 40-100 100-160	600 450 400	780 690 640	14 15 16
30CrMo	Thermal refining		≤100 100-300	410 390	620 590	16 15	196-240 196-240
35CrMo	Thermal refining		≤100 100-300 350-500 500-800	540 490 440 390	735 685 635 590	15 15 15 12	207-269 207-269 207-269 -
42CrMo	Thermal refining		≤100 100-160 160-250 250-500 500-750	650 550 500 460 390	900 800 750 690 590	12 13 14 15 16
35Mn2	Normalizing +tempering Thermal refining		≤100 100-300 ≤100 100-300	315 295 590 490	620 580 745 690	18 18 16 16	207-241 207-241 229-269 229-269
50CrVA	Untreated or heat-treated Quench +tempering	Plate Bar		1150	950 1300	12 10
35CrMoV	Thermal refining	Bar	100-200 200-240	745 705	880 860	12 12
40Cr	Thermal refining	Bar	≤100 100-300 300-500 500-800	540 490 440 345	735 685 685 590	15 14 10 8	241-286 241-286 229-269 217-255
20CrNiMo		Bar	≤15	785	980	9	197
15CrMn			≤50				HRC58-63
38CrMoAl	Quench +tempering	Bar		835	980	14	229
4Cr5MoSiV1	Quench +tempering	Bar	40-300				235
Cr5Mo1V	Tempering			576	1596		HRC46.7
9CrWMn	Annealing						228
Cr12MoV	Annealing						207-255
0Cr18Ni9				205	520	40	187
1Cr18Ni9Ti				205	520	40	187
GCr15	Quench +tempering	Bar	≤40	1666-1813	2156-2548		HRC63-68
T8	Annealing						187
T10	Annealing						197
T12	Annealing						207
9SiCr	Oil quench +tempering	Bar	≤50				HRC58-63
1Cr13	Quench +tempering			412	588	20
1Cr17	750-800℃Air cooled			245-285	412-632	20-57
W6Mo5Cr4V2	Untreated Annealing Quench +tempering						262 255 HRC63 or HRC64
W18Cr4V	Untreated Annealing Quench +tempering						269 255 HRC63

Mechanical properties
SS 14 1312

Structuralstrength

SS-steel	Condition	Delivery form	Thickness of material (mm)	ReL (N/mm2) ≥	ReH (N/mm2) ≥	Rm (N/mm2)	A5 % ≥	Hardness HB
1312-01	Normalized	Forged	≤ 50 (50)-250 (250)-500	220 200 200	240 220 220	360-460 360-(460) 360-(460)	27 25 24	100-130
1312-03	Untreated or heat-treated	Seamless tube	≤ 5 ≥ 5	240 220	260 240	360-490	24	-
1312-04	Untreated or heat-treated	Welded pipe	≤ 5 > 5	240 220	260 240	360-490	24	-
1312-06	Cold worked	Bar	≤ 50	370	-	≥ 440	10	(≥ 135)
1312-07	Cold worked	Seamless tube	≤ 5 > 5	410 390	-		11

SS 14 2134

Structuralstrength

SS-steel	Condition	Delivery form	Thickness of material (mm)	ReL (N/mm2) ≥	ReH (N/mm2) ≥	Rm (N/mm2)	A5 % ≥
2134-01	Normalized	Forged	-16 (16)-35 (35)-50 (50)-70	350 340 330 320	360 350 340 330	470-630	20
2134-03	Normalized	Seamless tube	-16 (16)-20	350 340	360 350	470-630	20
2134-04	Normalized	Welded pipe	-16 (16)-20	350 340	360 350	470-630	20

SS 14 2134

Impactstrength

Thickness of material (mm)	Test bar dimension	Temp (oC)	KV (J) ≥
6-(12) 12-70	5×10 10×10	-20 -20	18 27

SS 14 2172

Structuralstrength

SS-steel	Condition	Delivery form	Thickness of material (mm)	ReL (N/mm2) ≥	ReH (N/mm2) ≥	Rm (N/mm2)	A5 % ≥	Hardness HB
2172-01	Normalized	Forged	-250 (250)-500	290 280	300 290	470-620 470-610	21 20
2172-03	Untreated or heat-treated	Seamless tube	≤ 5 (5)-16 > 16	330 310 290	340 320 300	470-610	21
2172-04	Untreated or heat-treated	Welded pipe	≤ 5 (5)-16 > 16	330 310 290	340 320 300	470-610	21

SS 14 2225

Structuralstrength

SS-steel	Condition	Delivery form	Thickness of material (mm)	ReL (N/mm2) ≥	ReH (N/mm2) ≥	Rm (N/mm2)	A5 % ≥	Hardness HB
2225-03	Heat-treated	Bar	≤ 100	-	500	700-800	17	215-260

SS 14 2541

Structuralstrength

SS-steel	Condition	Delivery form	Thickness of material (mm)	ReL (N/mm2) ≥	ReH (N/mm2) ≥	Rm (N/mm2)	A5 % ≥	Hardness HB
2541-03	Heat-treated	Bar	≤ 100	-	700	900-1100	12	275-335

SS 14 2333

Structuralstrength

SS-steel	Condition	Delivery form	Thickness of material (mm)	Rp0,2 (N/mm2) ≥	Rm (N/mm2)	A5 % ≥	Hardness HB
2333-02	Solution heat treatment	Sheet, Strip	-30 (30)-50	210 190	500 500	40	(200) (200)
	Solution heat treatment	Bar	-50 (50)-100	210 190	500 500	40	(200) (200)
	Solution heat treatment	Welded pipe	-10 (10)-	210 190	500 500	40	(200) (200)

eat treatable aluminium alloy
SS	EN	GB	DIN	W.Nr	AA
4104	6063	?	AlMgSi0,5	3.3206	6063
4212-06	6082	?	AlMgSi1	2.2315	6082

emical composition
EN	Al	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti
6063	Residual	0,20-0,6	0,35	0,10	0,10	0,45-0,9	0,10	0,10	0,10
6082	Residual	0,7-1,3	0,50	0,10	0,40-1,0	0,6-1,2	0,25	0,20	0,10

EN AW-6082

Structuralstrength

Alloy	Delivery form	Condition	Thickness of material (mm)	Rp0,2 (N/mm2) ≥		Rm (N/mm2) ≥		A% ≥	A50% ≥
EN AW-6082	Extruded bar	O, H111 T4 T6	≤200 ≤200 ≤20 20<D≤150 200<D≤200	- 205 295 310 280 270	≤160 - - - - -	- 110 250 260 240 200	≤110 - - - - -	14 14 8 8 6 6	12 12 6 - - -
	Extruded pipe	O, H111 T4 T6	≤25 ≤25 ≤5 5<e≤25	- 205 290 310	≤160 - - -	- 110 250 260	≤110 - - -	14 14 8 10	12 12 6 8
	Extruded sections	O, H111 T4	all ≤25	- 205	≤160 -	- 110	≤110 -	14 14	12 12
		Open profile T5 T6	≤25 ≤25 ≤5 5<e≤25	270 290 310	- - - -	230 250 260	- - -	8 8 10	6 6 8
		Open profile T5 T6	≤25 ≤25 ≤5 5<e≤25	270 290 310	- - - -	230 250 260	- - -	8 8 10	6 6 8

Brass
SS	EN	GB	DIN	W.Nr	ASTM
5170	CuZn39Pb3	?	CuZn39Pb3

Chemical composition
SS	Cu %	Zn %	Pb %
5170	58	Residual	3

Structuralstrength

SS-steel	Rp0,2 (N/mm2) ≥	Rm (N/mm2)	A5 % ≥	Hardness HV
5170-00 -04	approx. 150 310-490	approx. 410 460-560	approx. 30 12-25	approx. 100 125-170

Bronze
SS	EN	GB	DIN	W.Nr	ASTM
5204-15		ZcuSn5Pb5-Zn5	CuSn5ZnPb		UNSC83600

Chemical composition
SS	Cu %	Sn %	Zn %	Pb %
5204	85	5	5	5

Structuralstrength

SS-steel	Rp0,2 (N/mm2) ≥	Rm (N/mm2)	A5 % ≥	Hardness HB
5204-00 -03 -15	- (90) (100)	- (230) (250)	- (15) (13)	- (60) (70)